In determining what glass or quartz capillary is right for you, please refer to the “Linear Absorption Coefficient µ cm-1” table. This table indicates the amount of radiation that is absorbed by the capillary during x-ray data collection.

For 0.1 mm to 2.5 mm capillaries the open end capillary tube base size is 3.0 +/- 0.2 mm OD x 0.2 +/- 0.15 mm Wall thickness. For 3.0 and 3.5 mm capillaries the open end capillary base size is about 4.4 mm OD x 0.25 mm Wall thickness. For 4.0 and 5.0 mm capillaries the open end capillary based size is about 6.0 x 0.25 mm.

The Diameter is measured  about 30 to 40 mm from the closed end (measuring instrument: LaserMicrometer LS 7500) The tolerances are as follows.

晶莹剔透的石英毛细管，壁厚极薄（壁厚约 10 微米）。毛细管的长度具有明确定义的直径，一端为漏斗形，另一端封闭。石英毛细管的壁厚为 0.01 mm，总长度为 80 mm +/-5 mm。石英毛细管的外径范围很广，从 0.1 mm 到 5.0 mm。它们旨在安装、固定和存储小分子和生物大分子晶体，用于 X 射线数据收集。毛细管也可用于晶体密度测量和晶体生长实验。可以使用蜡、环氧树脂或其他密封材料将毛细管紧密密封以防潮气和气体。

在确定适合您的玻璃或石英毛细管时，请参阅“线性吸收系数 µ cm-1”表。该表显示了在 X 射线数据采集过程中被毛细管吸收的辐射量。

对于 0.1 mm 至 2.5 mm 毛细管，开口端毛细管底座尺寸为 3.0 +/- 0.2 mm OD x 0.2 +/- 0.15 mm 壁厚。对于 3.0 和 3.5 mm 毛细管，开口端毛细管底座尺寸约为 4.4 mm OD x 0.25 mm 壁厚。对于 4.0 和 5.0 mm 毛细管，基于开口端毛细管的尺寸约为 6.0 x 0.25 mm。

直径从封闭端测量约 30 至 40 毫米（测量仪器：LaserMicrometer LS 7500） 公差如下。

Diameter    Tolerance              Minimum Diameter    Maximum Diameter

0.1 mm       +/-0.05 mm          0.05 mm                     0.15 mm
0.2 mm       +/-0.05 mm          0.15 mm                     0.25 mm
0.3 mm       +/-0.05 mm          0.25 mm                     0.35 mm
0.4 mm       +/-0.05 mm          0.35 mm                     0.45 mm
0.5 mm       +/-0.05 mm          0.45 mm                     0.55 mm
0.6 mm       +/-0.05 mm          0.55 mm                     0.65 mm
0.7 mm       +/-0.05 mm          0.65 mm                     0.75 mm
0.8 mm       +/-0.05 mm          0.75 mm                     0.85 mm
0.9 mm       +/-0.05 mm          0.85 mm                     0.95 mm
1.0 mm       -0.05 +0.25 mm    0.95 mm                     1.25 mm
1.5 mm       +/-0.25 mm          1.25 mm                     1.75 mm
2.0 mm       +/-0.25 mm          1.75 mm                     2.25 mm
2.5 mm       +/-0.05 mm          2.25 mm                     2.55 mm
3.0 mm       +/-0.25 mm          2.75 mm                     3.25 mm
3.5 mm       +/-0.25 mm          3.25 mm                     3.75 mm
4.0 mm       +/-0.25 mm          3.75 mm                     4.25 mm
5.0 mm       +/-0.25 mm          4.75 mm                     5.25 mm

Quartz Specifications
Glass type Fused silica / quartz glass
Density 2.2 g/cm³
Transformation temperature Tg= 1075 – 1210 degrees Celsius
Strain point approximately 1075 degrees Celsius
Annealing point approximately 1180 degrees Celsius
Softening point approximately 1730 degrees Celsius
Working point 1700 – 2100 degrees Celsius
Refractive index 1.46 589.3nm
Mohs hardness 5.5 – 6.5
Hydrolytic resistance, class 1 (DIN 12 111)
Acid resistance, class 1 (DIN 12 116)
Alkalai resistance, class 1 (DIN 52 322)
Chemical composition SiO₂ 99.99%
Trace elements
Al 16.00 ppm
Ca 0.80 ppm
Fe 0.80 ppm
K 0.90 ppm
Li 0.70 ppm
Na 0.90 ppm
Ti 1.50 ppm
Mg 0.10 ppm
Cu <0.05 ppm
Cr <0.05 ppm

Capillaries have only been tested at atmospheric pressure (760 mmHg (torr), 29.92 inHg, 14.696 psi). Use at other pressures has not been tested.

Quartz Capillary

Quartz Capillary

Quartz Capillary

Quartz Capillary

Quartz Capillary

Quartz Capillary

Quartz Capillary

Quartz Capillary

Quartz Capillary

Quartz Capillary

Quartz Capillary

Quartz Capillary

Quartz Capillary

Quartz Capillary

Quartz Capillary

Quartz Capillary